Abstract In this study, the effects of concretes which have 250, 300, 350 and 400 kg/m3 cement in per m3 and different voltage level application (0 V, 40 V, 60 V, 80 V and 100 V AC) on concrete maturity have been investigated. It has been researched if there is relationship with maturity and compressive strength on the concrete to which stress intensity has been applied. The electrical current has been applied on fresh concretes for 24 hours whose sizes are 10 × 10 × 35 cm. Their internal temperatures of concretes have been recorded and maturity values have been calculated. It has been concluded that AC stress intensity can be used to accelerate maturity through obtaining optimum degree on concrete’s internal temperature without any compressive strength lost.

Resumen En este estudio, se investigaron los efectos de los hormigones que tienen 250, 300, 350 y 400 kg/ m3 de cemento y la aplicación de diferentes niveles de voltaje (0 V, 40 V, 60 V, 80 V y 100 V AC) en la madurez del concreto. Se ha investigado si existe una relación con la madurez y la resistencia a la compresión en el concreto al que se ha aplicado la intensidad de tensión. La corriente eléctrica se ha aplicado sobre hormigones frescos durante 24 horas cuyos tamaños son 10 × 10 × 35 cm. Se han registrado las temperaturas internas de los hormigones y se han calculado los valores de madurez. Se ha llegado a la conclusión de que la intensidad de tensión de CA se puede utilizar para acelerar la madurez a través de la obtención de un grado óptimo en la temperatura interna del concreto sin pérdida de resistencia a la compresión.

Abstract This paper focuses on the electrical, physical and mechanical characterization of the ancient mortar (khorasan mortar) materials of precious structures, the Ali Paşa bathhouse, Çandarlı İbrahim Paşa bathhouse, Hasan Paşa bathhouse, Iznik Castle and Tophane rampart historical constructions located in the West of Turkey, in Bursa. An exhaustive description of the materials has been obtained to enriching the knowledge on historical construction materials. The definition of the physical and mechanical properties of the materials, sophisticated laboratory tests were performed such as compressive strength, point loading, weight loss in acid, specific porosity, density and water absorption tests. Microstructure investigations and electrical resistivity measurements were also performed on the ancient mortars. The good correlations were obtained between electrical resistivity and mechanical properties of historical mortars as result of relations between them. The experimental investigation has allowed a better understanding of the remote origin of these structures.

Resumen Este documento se centra en la caracterización eléctrica, física y mecánica de materiales de mortero antiguo (mortero Khorasan) de estructuras preciosas, la casa de baños Ali Paşa, la casa de baños Çandarlı İbrahim Paşa, la casa de baños Hasan Paşa, el castillo Iznik y el dique Tophane en la histórica Edificios situados en el oeste de Turquía, en Bursa. Se ha obtenido una descripción exhaustiva de los materiales para enriquecer el conocimiento sobre materiales de construcción históricos. La definición de las propiedades físicas y mecánicas de los materiales, se llevaron a cabo sofisticadas pruebas de laboratorio, tales como resistencia a la compresión, carga puntual, pérdida de peso ácida, porosidad específica, densidad y pruebas de absorción de agua. Investigaciones de microestructura y medidas de resistividad eléctrica también se realizaron en los morteros viejos. Se obtuvieron buenas correlaciones entre la resistividad eléctrica y las propiedades mecánicas de los morteros históricos como resultado de las relaciones entre ellos. La investigación experimental ha permitido una mejor comprensión del origen remoto de estas estructuras.

In this study, influence of curing condition and fly ash content on properties of pre-fabricated concrete interlocking blocks (PCIBs) were investigated. The blocks were produced with crushed sand stone (fine) and crushed stone (coarse) as aggregate. Also, fly ash was added to mixtures in different ratio by replacing the cement from 0 to 30%. PCIBs were cured in three different types as steam cure, water-pool cure and wet cure. Compressive strength, tensile splitting strength, density, apparent porosity, water absorption by weight and abrasion resistance of PCIBs was determined. When comparing the PCIBs, the use of wet cure results in lower physical and mechanical properties after 28 days. By contrast, water- pool and steam cure gives better result on mechanical and physical properties. Also, replacement of cement with fly ash (from 10% to 20%) has a significant effect in increasing important properties of PCIBs.

En este estudio, la influencia de la curación de la condición y el contenido de cenizas volantes sobre las propiedades del hormigón prefabricado Bloques entrelazados (PCIBs) fueron investigados. Los bloques fueron producidos con arena de piedra triturada (fina) y piedra triturada (grueso) como agregado. Además, cenizas fueron añadidas a las mezclas en diferente relación, reemplazando el cemento desde 0 a 30%. Los PCIBs fueron curados en tres tipos diferentes como: cura de vapor, piscina de agua cura y cura húmeda. Resistencia a la compresión, resistencia a la tracción indirecta, densidad, porosidad aparente, absorción de agua por el peso y la resistencia a la abrasión de PCIBs fue determinadas. Cuando se comparan los PCIBs, el uso de la cura húmeda se traduce en la reducción de propiedades físicas y mecánicas, después de 28 días. Por el contrario, la piscina de agua y vapor cura da mejor resultado en las propiedades mecánicas y físicas. Además, la sustitución de cemento con ceniza volante (del 10% al 20%) tiene un efecto significativo en el aumento de propiedades importantes de PCIBs.

<title>Abstract</title><p>Polymer surface coatings provide superior adhesion to substrates, some flexibility and corrosion resistance. On the other hand, 400,000 ton of boron wastes are generated each year. We have developed polymer composites based on epoxy resins containing up to 50 wt. % of boron wastes and determined their pin-on-disk dynamic friction, wear, Shore D hardness and surface roughness. The hardness and wear resistance increase with increasing boron waste concentration. An equation, with parameters dependent on the load, relating wear rate to hardness is provided. Dynamic friction increases with increasing surface roughness, as represented by the equation. Further, dynamic friction is an increasing function of the wear rate. Micrographs of pure epoxy without fillers shows traces after pin-on-disk testing, with tears, breaks and cracks. For the composites, we observe simpler and relatively homogeneous surfaces.</p>